| Brand Name: | TANKII |
| Model Number: | FeCrAl |
| Certification: | ISO9001 SGS |
| Place of Origin: | Shanghai, China |
| MOQ: | 100 KG |
| Price: | negotiable |
| Payment Terms: | L/C, T/T, Western Union |
| Supply Ability: | 200 Tons per month |
| Delivery Time: | 7-20 days |
| Packaging Details: | Wooned Case |
| material: | FeCrAl alloy |
| Resistivity: | 1.45 |
| surface: | Bright |
| sample: | accepted small order |
| thickness: | 0.01mm Min. |
| Company Info. |
| Shanghai Tankii Alloy Material Co.,Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Aluchrom Y heating resistor foil
ASTM B603, DIN 17470, JIS C2520, GB/T1234.
Our advantage: High quality, short delivery time, small MOQ.
Characteristics: Stable performance; Anti-oxidation; Corrosion
resistance; High temperature stability; Excellent coil-forming
ability; Uniform and beautiful surface condition without spots.
Usage: Resistance heating elements; Material in metallurgy;
Household appliances; Mechanical manufacturing and other
industries.
Packing detail: Spool, coil, wooden case(as per client's
requiryment)
Shanghai TANKII ALLOY MATERIAL Co., Ltd.
FECRAL AND ALCHROME ALLOY PRODUCER IN China, MOST PROFESSIONAL IN
THE WORLD.
Alloy | Cr% | Al% | Fe% | Re% | Nb% |
0Cr21Al6Nb | 21.0-23.0 | 5.0-7.0 | Bal. | Adequacy | 0.5 |
Properties
Alloy | Specific Resistance (at 20° C) (µ Ω -m) | Hardness HB | Linear Expansion Coeff. (T=20 - 1000° C) x10-6 | Maximum Operating Temperature of Element (° C) |
0Cr21Al6Nb | 1.45± 0.07 | 200-260 | 16.0 | 1350 |
| rand name | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main chemical composition% | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| RE | opportune amount | opportune amount | opportune amount | opportune amount | opportune amount | opportune amount | opportune amount | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max.continuous service temp.of element (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity μΩ.m,20ºC | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density (g/cm3 ) | 7.4 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
| Thermal conductivity KJ/m.h.ºC | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
| Coefficient of lines expansion α×10-6/ºC | 15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
| Melting pointºC | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength Mpa | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture % | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area % | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
|
19*0.574 0Cr25Al5 Stranded Rope Wire / Fecral Wire Heating Resistance Equipments
7.1 G / M3 Strip Heater Element 0cr21al6nb For High Temperature Industrial Furnace
0cr27al7mo2 Fecral Alloy Heat Resistant Wire For Electric Stove / Spring Heating
Heating Strip FeCrAl Alloy 0Cr21Al6Nb High Resistivity Oxidation Surface 2.0x20mm
High Resistivity 1Cr13Al4 FeCrAl Strip Thickness 0.7mm With 1200mm Width
1Cr13Al4 FeCrAl Alloy Strip Bright Surface For Automobile Exhaust Purifier
1Cr13Al4 FeCrAl Alloy Strip 0.7*1100mm Three Way Catalytic Converter Use
SGS Certified FeCrAl Alloy Strip With Big Width 100~1000mm Honeycomb Exhaust Purifier Use
0cr21al4 Fecral Heating Element Bright Fecral Resistance Wire
ASTM B603 Diameter 10mm Ni80cr20 FeCrAl Alloy For Metallurgy